作者吴庆文,刘艳娟（2019）在《铁尾矿轻质保温砖的研制》一文中研究指出：以铁尾矿和紫木节粘土为主要原料,加入成孔剂,经研磨混合、成型、干燥及烧成,可制备铁尾矿轻质保温砖。实验结果表明:所选的白云石、碳酸钙、碳酸镁及煤粉四种成孔剂,较为合理的成孔剂为白云石。加入量20wt.%、烧成温度1100℃、保温时间20 min时,制备的轻质保温砖气孔率达65.7 vol.%,抗压强度为7.1 MPa,符合MJ5.0标准(强度≥5.0 MPa)要求;体积密度为1.10 g/cm~3,符合轻质保温砖的密度要求(0.75-1.20 g/cm~3)。可作为民用等建筑物保温材料。
Abstract
yi tie wei kuang he zi mu jie nian tu wei zhu yao yuan liao ,jia ru cheng kong ji ,jing yan mo hun ge 、cheng xing 、gan zao ji shao cheng ,ke zhi bei tie wei kuang qing zhi bao wen zhuan 。shi yan jie guo biao ming :suo shua de bai yun dan 、tan suan gai 、tan suan mei ji mei fen si chong cheng kong ji ,jiao wei ge li de cheng kong ji wei bai yun dan 。jia ru liang 20wt.%、shao cheng wen du 1100℃、bao wen shi jian 20 minshi ,zhi bei de qing zhi bao wen zhuan qi kong lv da 65.7 vol.%,kang ya jiang du wei 7.1 MPa,fu ge MJ5.0biao zhun (jiang du ≥5.0 MPa)yao qiu ;ti ji mi du wei 1.10 g/cm~3,fu ge qing zhi bao wen zhuan de mi du yao qiu (0.75-1.20 g/cm~3)。ke zuo wei min yong deng jian zhu wu bao wen cai liao 。
论文参考文献
论文详细介绍
论文作者分别是来自陶瓷学报的吴庆文,刘艳娟，发表于刊物陶瓷学报2019年01期论文，是一篇关于铁尾矿论文,成孔剂论文,轻质保温砖论文,陶瓷学报2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自陶瓷学报2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：铁尾矿论文; 成孔剂论文; 轻质保温砖论文; 陶瓷学报2019年01期论文;