本文主要研究内容
作者张盛,张圣斌,刘巍,庞婧,卢文壮（2019）在《金刚石衬底的V2O5薄膜激光损伤阈值研究》一文中研究指出：目的探究V2O5薄膜厚度对其抗激光损伤性能的影响。方法通过射频反应磁控溅射法在光学级单晶金刚石衬底表面制备了不同膜厚的V2O5薄膜。采用脉宽为10 ns、波长为1064 nm的脉冲激光器对薄膜样品进行光学响应曲线测试,测得薄膜相变前后透过率变化情况及相变开关时间,以判断薄膜是否发生损伤,并根据损伤几率得到激光损伤阈值。结果实验制备的薄膜为组分单一的多晶V2O5,在（001）面具有明显择优取向。同一膜厚下（350 nm）,随着激光能量密度的增加,薄膜的相变关闭时间由1.48 ms单调减小至0.64 ms,相变回复时间则由11.6 ms单调增加至20.4 ms,相变后的透过率由19%单调减小至8%,回复后的透过率由77%单调减小至51%。薄膜膜厚在150～550 nm的范围内,其激光损伤阈值随着膜厚的增加呈现出先增后减的趋势;当膜厚等于250 nm时,激光损伤阈值达到最大值,为260 mJ/cm2;膜厚为550 nm时,激光损伤阈值最小,仅为209 mJ/cm2。结论 V2O5薄膜厚度对其抗激光损伤性能具有较大的影响,合理地控制膜厚,能够有效提高激光损伤阈值,从而提高基于金刚石衬底的V2O5薄膜的抗激光损伤能力。
Abstract
mu de tan jiu V2O5bao mo hou du dui ji kang ji guang sun shang xing neng de ying xiang 。fang fa tong guo she pin fan ying ci kong jian she fa zai guang xue ji chan jing jin gang dan chen de biao mian zhi bei le bu tong mo hou de V2O5bao mo 。cai yong mai kuan wei 10 ns、bo chang wei 1064 nmde mai chong ji guang qi dui bao mo yang pin jin hang guang xue xiang ying qu xian ce shi ,ce de bao mo xiang bian qian hou tou guo lv bian hua qing kuang ji xiang bian kai guan shi jian ,yi pan duan bao mo shi fou fa sheng sun shang ,bing gen ju sun shang ji lv de dao ji guang sun shang yu zhi 。jie guo shi yan zhi bei de bao mo wei zu fen chan yi de duo jing V2O5,zai （001）mian ju you ming xian ze you qu xiang 。tong yi mo hou xia （350 nm）,sui zhao ji guang neng liang mi du de zeng jia ,bao mo de xiang bian guan bi shi jian you 1.48 mschan diao jian xiao zhi 0.64 ms,xiang bian hui fu shi jian ze you 11.6 mschan diao zeng jia zhi 20.4 ms,xiang bian hou de tou guo lv you 19%chan diao jian xiao zhi 8%,hui fu hou de tou guo lv you 77%chan diao jian xiao zhi 51%。bao mo mo hou zai 150～550 nmde fan wei nei ,ji ji guang sun shang yu zhi sui zhao mo hou de zeng jia cheng xian chu xian zeng hou jian de qu shi ;dang mo hou deng yu 250 nmshi ,ji guang sun shang yu zhi da dao zui da zhi ,wei 260 mJ/cm2;mo hou wei 550 nmshi ,ji guang sun shang yu zhi zui xiao ,jin wei 209 mJ/cm2。jie lun V2O5bao mo hou du dui ji kang ji guang sun shang xing neng ju you jiao da de ying xiang ,ge li de kong zhi mo hou ,neng gou you xiao di gao ji guang sun shang yu zhi ,cong er di gao ji yu jin gang dan chen de de V2O5bao mo de kang ji guang sun shang neng li 。
论文参考文献
论文详细介绍
论文作者分别是来自表面技术的张盛,张圣斌,刘巍,庞婧,卢文壮，发表于刊物表面技术2019年05期论文，是一篇关于激光致盲论文,薄膜论文,膜厚论文,损伤阈值论文,金刚石衬底论文,表面技术2019年05期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自表面技术2019年05期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。