本文主要研究内容
作者（2019）在《Hollow Nanocages of NixCo1-xSe for Efficient Zinc–Air Batteries and Overall Water Splitting》一文中研究指出：Developing Earth-abundant,highly efficient,and anticorrosion electrocatalysts to boost the oxygen evolution reaction（OER）,oxygen reduction reaction（ORR）,and hydrogen evolution reaction（HER） for the Zn–air battery（ZAB） and for overall water splitting is imperative.In this study,a novel process starting with Cu2O cubes was developed to fabricate hollow NixCo1-xSe nanocages as trifunctional electrocatalysts for the OER,ORR,and HER and a reasonable formation mechanism was proposed.The Ni0.2Co0.8Se nanocages exhibited higher OER activity than its counterparts with the low overpotential of 280 mV at 10 mA cm-2.It also outperformed the other samples in the HER test with a low overpotential of 73 mV at 10 mA cm-2.As an air–cathode of a self-assembled rechargeable ZAB,it exhibited good performance,such as an ultralong cycling lifetime of > 50 h,a high round-trip efficiency of 60.86%,and a high power density of 223.5 mW cm-2.For the application in self-made all-solid-state ZAB,it also demonstrated excellent performance with a power density of 41.03 mW cm-2 and an open-circuit voltage of 1.428 V.In addition,Ni0.2Co0.8Se nanocages had superior performance in a practical overall water splitting,in which only 1.592 V was needed to achieve a current density of 10 mA cm-2.These results show that hollow NixCo1-xSe nanocages with an optimized Ni-to-Co ratio are a promising cost-effective and high-efficiency electrocatalyst for ZABs and overall water splitting in alkaline solutions.
Abstract
Developing Earth-abundant,highly efficient,and anticorrosion electrocatalysts to boost the oxygen evolution reaction（OER）,oxygen reduction reaction（ORR）,and hydrogen evolution reaction（HER） for the Zn–air battery（ZAB） and for overall water splitting is imperative.In this study,a novel process starting with Cu2O cubes was developed to fabricate hollow NixCo1-xSe nanocages as trifunctional electrocatalysts for the OER,ORR,and HER and a reasonable formation mechanism was proposed.The Ni0.2Co0.8Se nanocages exhibited higher OER activity than its counterparts with the low overpotential of 280 mV at 10 mA cm-2.It also outperformed the other samples in the HER test with a low overpotential of 73 mV at 10 mA cm-2.As an air–cathode of a self-assembled rechargeable ZAB,it exhibited good performance,such as an ultralong cycling lifetime of > 50 h,a high round-trip efficiency of 60.86%,and a high power density of 223.5 mW cm-2.For the application in self-made all-solid-state ZAB,it also demonstrated excellent performance with a power density of 41.03 mW cm-2 and an open-circuit voltage of 1.428 V.In addition,Ni0.2Co0.8Se nanocages had superior performance in a practical overall water splitting,in which only 1.592 V was needed to achieve a current density of 10 mA cm-2.These results show that hollow NixCo1-xSe nanocages with an optimized Ni-to-Co ratio are a promising cost-effective and high-efficiency electrocatalyst for ZABs and overall water splitting in alkaline solutions.
论文参考文献
论文详细介绍
论文作者分别是来自Nano-Micro Letters的，发表于刊物Nano-Micro Letters2019年02期论文，是一篇关于,Nano-Micro Letters2019年02期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Nano-Micro Letters2019年02期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。